FUEL INJECTOR ASSEMBLY LEAKAGE
NHTSA Engineering Analysis EA98007 - closed, opened 1998-03-10 and involving the CHRYSLER CHRYSLER.
NHTSA investigation EA98007 is a Engineering Analysis opened on 1998-03-10 and currently closed. The subject of record is CHRYSLER CHRYSLER, which places this file inside the Office of Defects Investigation queue for CHRYSLER. Latest activity on this investigation was logged on 1999-02-01 - NHTSA updates that field whenever an Information Request goes out, a supplement is filed, or a status change is recorded in the public docket.
An Engineering Analysis like EA98007 is the deeper technical phase that follows a PE. NHTSA requests design, warranty, and field-failure data from the manufacturer, conducts its own testing when needed, and determines whether the evidence supports a safety defect finding that would compel a recall.
Investigators summarized the matter as follows: "NITRILE RUBBER SEALS USED IN THE FUEL RAIL ASSEMBLIES OF THE SUBJECT VEHICLES AT THE SUPPLY, RETURN, AND CROSSOVER TUBE FITTINGS, AND AT THE PRESSURE REGULATOR FAIL, RESULTING IN FUEL LEAKAGE IN THE ENGINE COMPARTMENT. A..." Investigations are the early-warning layer of the federal auto-safety system, sitting upstream of formal recalls and defect orders. Whether this one closes without action or escalates into an Engineering Analysis, the full history stays in the ODI archive so researchers, litigators, and buyers can pull the paper trail at any time. Related CHRYSLER files, listed below, give context on whether this is an isolated concern or part of a broader pattern across the brand.
Investigation Summary
NITRILE RUBBER SEALS USED IN THE FUEL RAIL ASSEMBLIES OF THE SUBJECT VEHICLES AT THE SUPPLY, RETURN, AND CROSSOVER TUBE FITTINGS, AND AT THE PRESSURE REGULATOR FAIL, RESULTING IN FUEL LEAKAGE IN THE ENGINE COMPARTMENT. ALSO, THE OUTLET (RIGHT) FUEL RAIL MAY LEAK FROM CRACKS AT CERTAIN MOLD GATES IN THE THERMOSET RAIL MATERIAL. CHRYSLER WILL RECALL THE SUBJECT VEHICLES AND STATED THAT IT INTENDS TO REPLACE THE O-RINGS WITH FLUOROCARBON O-RING HAVING GREATER HEAT RESISTANCE CAPABILITY AND ATTACH REINFORCEMENTS TO THE RAIL IN THE AREAS WHERE THE CRACKING CONCERN HAS BEEN KNOWN TO OCCUR MOST FREQUENTLY. RAILS THAT ARE ALREADY CRACKED WILL BE REPLACED BY NEW, REINFORCED RAILS.
About This Investigation Type
An Engineering Analysis (EA) is the in-depth phase following a Preliminary Evaluation. NHTSA engineers conduct testing, collect data from manufacturers, and perform detailed technical analysis to determine whether a safety defect exists. An EA may lead to a voluntary recall by the manufacturer or, in rare cases, a mandatory recall order.
Other CHRYSLER Investigations
Recall 23V-413 Post Remedy Failures
Intermittent Loss of Electric Power Steering
Recall 19V-293 Post Remedy Failures
Engine Stall With Intermittent Restart
Loss of motive power due to an internal wiring connector short.
Data from NHTSA Office of Defects Investigation. Cross-references: NHTSA recall campaign API and NHTSA FARS where fatality records overlap. PlainCars does not rate or recommend vehicles. about how PlainCars sources NHTSA data.
Read our methodology - how this data is sourced, computed, and verified.